Zhenjiang Sanwei Conveying Equipment Co.,Ltd
HOME | ABOUT US | PRODUCTS | OUR DEVELOPMENT | FAQ | CONTACT US | SITEMAP | 中文版
Bucket Elevator Components
Elevator Buckets
Elevator Belts
Elevator Bolts
Belt Fasteners
Belt Conveyor Components
Conveyor Belts
Impact Bars / Impact Beds
Conveyor Idlers / Rollers
Screw Flights/ Auger Flighting
Continuous Screw Flights
Sectional Screw Flights
Drag Conveyor Components
Conveyor Chains and Flights
Chain Sprockets
Nylon Gear Wheels
Parts for Sieves and Screens
Sieve Cleaners and Pan Cleaners
Sieve Cleaning Balls
Engineering Plastic Products
UHMWPE
HDPE
NYLON
PTFE
POM
 
 
 Heat Resistant and High Temperature Resistant Belt Products > Belt Conveyor Components > Conveyor Belt
  FAQ PDF download
Heat Resistant and High Temperature Resistant Belt Heat Resistant and High Temperature Resistant Belt

FEATURES
The carcass is made from high modulus, low shrink Polyester fabric, Cotton fabric, Cotton or Terylene/Cotton fabric.
Choosing heat resistant or high temperature resistant rubber material as the cover rubber, the belt is manufactured by forming and vulcanizing.

APPLICATIONS
Suitable for using in the field of metallurgy industry and construction where there is the need to convey hot materials such as sinter, coke, cement clinker as well as numerous other industries that need High Temperature Resistant Conveyor Belting.

BELT TYPES
Heat Resistant
T1: Suitable for using at temperature from 60-125 deg C continuous rated, and temperature of 150 deg C intermittently.
T2: Suitable for using at temperature from 125-150 deg C continuous rated, and temperature of 180 deg C intermittently.
High Temperature Resistant
T3: Suitable for using at temperatures up to 180 deg C continuous rated, and temperature of 230 deg C intermittently.

Grade Fabric Type Structure
Cover Rubber
Thickness(mm)
Belt Width
(mm)
Belt
Length
(M)
Warp Weft Top Top
T1
T2
Cotton/Cotton CC-56 Cotton Cotton ≥4.5 1.0~4.5 300~1500 ≤300
Terelyne/Cotton TC-70 Terylene Cotton Cotton
EP80~EP400 Terylene Nylon
T3 TNGEP80~TNGEP400 Low Shrinkage Terylene Nylon ≥6.0

TECHNICAL DATA
Standard: In accordance to HG2297-92
Physical & Mechanical Performance after heating and aging test

Item Grade
T1 T2 T3
Value
Hardness ( IRHD) Difference after aging --- --- ±20
( IRHD) Max value after aging 85
Tensile Strength Variable Rate of Performance (%) ≤ 25 30 40
Minimum Value after Aging (MPa) 12 10 5
Elongation at Break Variable Rate of Performance (%) ≤ 50 55
Minimum after Aging (MPa) 200 180
Abrasion Loss                      (mm³) 200 250 250

Adhesion Strength-Ply to Ply

Fabric Type Item Canvas Ply to
Canvas Ply
Cover to Canvas Ply
Cover Rubber
Thickness
≤1.50mm
Cover Rubber
Thickness
>1.50mm
Cotton-CC56
Terylene Cotton-TC70
Average Value of Samples
in Warp ≥
3.0 2.20 2.60
Minimum Value of Samples
in Warp
2.0 1.60 2.0
Polyester-EP
Polyester-TNG EP
Average Value of Samples
in Warp ≥
6.0 3.80 4.50
Minimum Value of Samples
in Warp
3.50 3.20 3.50

How to Get Proper Belt?

Following factors need to be considered to get proper belt
·Materials temperature, shape, adhesive parameter, etc.
·When conveying big size materials such as sinter, coke etc with high temperature around 150 degree C,also with small contact area with the belt, the belt surface temperature will be between 60-80 degree C.
·It will be small difference in temperature between belt surface and material when conveying low adhesion materials such as cement, flour etc.
·Belt surface temperature affects directly belt life time, so that full investigation on belt surface temperature need to be done before choosing the proper grade for the heat and high temperature resistant belt.

Maintenance and Inspection
·Keep regularly inspecting and consistent measuring to be sure belt surface temperature at reasonable level.
·We strongly recommend that heat resistant belts to be cooled on the return course by water spray or other suitable cooling methods. Always try to evenly distribute materials across the width of the belt so as to reduce the heat concentration in the center of the belt.
·Oil contained in cooling water or in materials will be very harmful to the life of belt, even worse than heat itself, thus the oil must be prevented. The heat materials should be unloaded once belt stops working.
·Hot vulcanization joint is recommended.

Conveyor belt production
Conveyot belt

 

Copyright (C) 1989 - 2012 Zhenjiang Sanwei Conveying Equipment Co., Ltd All rights reserved --- Sitemap

Address :No.1, Panzong Road, Zhenjiang Hi-Tech Industrial Park, Zhenjiang,Jiangsu, China 212009

 

ENGINEERING PLASTICS BUCKET ELEVATOR COMPONENTS BELT CONVEYOR COMPONENTS DRAG CONVEYOR COMPONENTS PARTS FOR SIEVES AND SCREENS SCREW FLIGHTS /
AUGER FLIGHTING
UHMWPE Elevator Buckets Impact Bars Conveyor Chains and Flights Pan Cleaners Continuous Augers
HDPE Elevator Bolts Conveyor Belts Chain Sprockets Sieve Cleaners Sectional Augers
PTFE Belt Fasteners Conveyor Idlers Nylon Gear Wheels Sieve Rubber Cleaning Balls
Nylon Elevator Belts        
POM          